Journal
CHEMICAL ENGINEERING JOURNAL
Volume 346, Issue -, Pages 182-192Publisher
ELSEVIER SCIENCE SA
DOI: 10.1016/j.cej.2018.04.033
Keywords
Microsperical catalyst; MnOx-CeO2-Al2O3 mixed oxide; Monolithic honeycomb catalyst; Selective catalytic reduction; Denitration process; Spray drying method
Categories
Funding
- National High Technology Research and Development Program of China (863 program) [2015AA03A401]
- Program for Changjiang Scholars and Innovative Research Team in University [IRT_15R46]
- Program of Science and Technology Innovation Team in Bingtuan [2015BD003]
Ask authors/readers for more resources
MnOx-CeO2-Al2O3 microspheres (MSs) were successfully designed and synthesized via spray drying (SD) and easily used for monolithic honeycomb catalyst (MHC). The as-obtained MnOx-CeO2-Al2O3 (SD) catalyst exhibited a great BET surface area of 201.4 m(2)/g, a pore volume of 0.29 cm(3)/g, and an average pore diameter of 5.8 nm. Furthermore, the MnOx-CeO2-Al2O3 (SD) MSs delivered much more O-latt sits resulting in enhanced catalytic activity at low temperature. The MnOx-CeO2-Al2O3 (SD) performed excellent NOx conversion of 97.4% and N-2 selectivity of 94.5% at 150 degrees C with a gas hourly space velocity (GHSV) of 15,000 h(-1), and NOx concentration of 500 ppm. Even at 50 degrees C and 100 degrees C, the titled product still exhibited great N-2 selectivity of 95.5% and 96.1%, respectively, corresponding to the NOx conversion of 55% and 98.0%, respectively. The MnOx-CeO2Al2O3 (SD) monolithic honeycomb catalyst (MHC) was prepared by vacuum-impregnation method. The MnOxCeO2-Al2O3 (SD-MHC) delivered NOx conversion of 93% at 150 degrees C with a GHSV of 2000 h(-1), and NOx concentration of 500 ppm. Even at 50 degrees C and 100 degrees C, the titled product still performed NOx conversion of 55% and 83%, respectively. The MnOx-CeO2-Al2O3 (MHC) performed great catalytic activity in the low temperature arrange from 50 to 150 degrees C and presented potential application in stationary industrial installations.