CHEMCATCHEM
Volume 10, Issue 13, Pages 2845-2857Publisher
WILEY-V C H VERLAG GMBH
DOI: 10.1002/cctc.201800327
Keywords
cobalt; core-shell structure; nanocatalyst; nanomaterials; silicon dioxide
Categories
Funding
- NSFC [21173118, 21373110]
- MSTC [2013AA031703]
Ask authors/readers for more resources
Dry reforming of methane has been systematically investigated over a series of x-Co@SiO2-y catalysts where x is the Co particle size ranging from 11.1 to 121.3nm while y denotes the silica shell thickness ranging from 6.0 to 21.9nm. Various techniques including TEM, XRD, H-2-TPR/-TPD, XPS, BET, O-2-TPO, TG, and H-2-TPSR-MS were employed to characterize physicochemical properties of catalysts. H-2-TPR and XPS results indicate that the core-shell interaction is dependent on the core size: the smaller the Co particle size is; the stronger the core-shell interaction. The investigations employing H-2-TRSR-MS and XPS on the spent catalysts demonstrated that a fraction of metallic Co was re-oxidized on a large-core catalyst such as 121.3-Co@SiO2-72.2 during the reaction, and such oxidation leads to lower catalytic activity and stability. O-2-TPO results indicated that the catalyst with smaller core size caused significant coking. TG analysis together with TEM investigation on the used samples suggested that carbon deposition is notably core-size-dependent and responsible for deactivation of the small-core catalyst. Among various core-shell structured catalysts, 27.8-Co@SiO2-14.3 showed superior activity and durability, owing to the well-balanced property between coking and anti-oxidation of Co cores.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available