Journal
CATALYSTS
Volume 7, Issue 9, Pages -Publisher
MDPI AG
DOI: 10.3390/catal7090246
Keywords
ethanol oxidation reaction; direct ethanol fuel cell; tandem catalyst; Pt/Rh/SnOx; infrared reflection-absorption spectroscopy; selective CO2 production
Categories
Ask authors/readers for more resources
To elucidate the atomic arrangement of a Pt-Rh-Sn ternary catalyst with a high catalytic activity for ethanol oxidation reaction (EOR) and high CO2 selectivity, we prepared a tandem Pt/Rh/SnOx, in which a Rh adlayer was deposited on a Pt substrate (Rh coverage: 0.28), followed by depositing several layers of SnOx only on the Rh surface (Sn coverage: 0.07). For reference, Sn was randomly deposited on the Rh-modified Pt (Pt/Rh) electrode whose Rh and Sn coverages were 0.22 and 0.36 (random Pt/Rh/SnOx). X-ray photoelectron spectroscopy demonstrated that Pt and Rh were metallic, and Sn was largely oxidized. Both Pt/Rh/SnOx electrodes were less positive in onset potential of EOR current density and higher in EOR current density than Pt and Rh/Pt electrodes. In situ infrared reflection-absorption spectroscopy demonstrated that the tandem Pt/Rh/SnOx electrode did not produce acetic acid, but produced CO2 in contrast to the random Pt/Rh/SnOx, suggesting that a tandem arrangement of Pt, Rh and SnOx, in which the Pt and SnOx sites were separated by the Rh sites, was effective for selective CO2 production. In the electrostatic electrolysis at 0.5 V vs. RHE, the tandem Pt/Rh/SnOx electrode exhibited higher EOR current density than the Pt and Pt/Rh electrodes after 1.5 h.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available