JOURNAL OF MATERIALS CHEMISTRY A
Volume 5, Issue 11, Pages 5568-5576Publisher
ROYAL SOC CHEMISTRY
DOI: 10.1039/c6ta11001k
Keywords
-
Funding
- National Natural Science Foundation of China [51271135]
- Fundamental Research Funds for the Central Universities
- Natural Science Foundation of Shanxi Province [2015JM5166]
- Scientifc Research Foundation for the Returned Overseas Chinese Scholars, State Education Ministry
Ask authors/readers for more resources
Flexible solid-state asymmetric supercapacitors (FSASCs) have been considered to be excellent energy storage components for flexible and portable electronic devices. Pseudocapacitive materials involved in FSASCs may bring in high capacitance and energy density which are crucial for their practical applications. In this work a kind of NiCO2O4 pseudocapacitive cathode material with an urchin-like hollow micro-sphere structure (UHMS) was designed and synthesized. Due to the high proportion of active sites and fluent ionic channels created by the UHMS structure the as-prepared NiCO2O4 UHMS sample shows an enhanced specific capacitance of about 942.2 F g-1 at 0.5 A g-1 and desirable rate capability. In addition a pseudocapacitive anode material FeSe2 with a hierarchical snowflake (SF) structure was also prepared by an anion exchange reaction through a unique morphological reconstruction process. The obtained material shows a much higher capacitance (304 F g-1 at 0.5 A g-1) and better rate capability than its parent material (micro dendritic Fe2O3). A FSASC was fabricated using the NiCO2O4 cathode and FeSe2 anode on a simple flexible current collector prepared from scotch tape and graphite paper and it delivered a high operating voltage up to 1.5 V an energy density of 10.4 W h kg-1 a maximum power density of 1.2 kW kg-1 and long term stability for 1000 cycles. Such an impressive FSASC is totally based on pseudocapacitance in both electrodes and would be a promising candidate for use in flexible and wearable electronic devices.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available