While possessing potential advantages as electrodes for lithium-ion batteries, SnO2@carbon composites have been suffering from one common drawback - aggregation of Sn particles during the repeated alloying-dealloying cycles and the resulting pulverization issue. We combat this issue through the fabrication of honeycomb-like SnO2@carbon nanoflakes (SnO2@CNFs) that are able to confine SnO2 nanoparticles within well-separated carbon cavities, so that the Li-Sn alloying-dealloying reaction occurs in the independent microreactors thus avoiding aggregation of Sn metal particles formed. The SnO2 particle size, loading amount and the coverage density are controlled by adjusting the weight ratio between the tin precursor and the CNF. Transmission electron microscopy confirms that the highly graphitic honeycomb-like CNF matrix efficiently buffers and accommodates volume changes of the Li-Sn alloy. Used as anode materials for lithium-ion batteries, the SnO2@CNFs with 66.0 wt% SnO2 display the highest lithiumstorage capacity, delivering a discharge capacity of 940 mA h g(-1) after 150 cycles at 200 mA g(-1). For the long-term and high-rate applications, the SnO2@CNFs with 41.5 wt% SnO2 show the best electrochemical performance, delivering a discharge capacity of 400 mA h g(-1) at 1 A g(-1) after 500 cycles.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available