CELLULOSE
Volume 24, Issue 11, Pages 5133-5145Publisher
SPRINGER
DOI: 10.1007/s10570-017-1462-z
Keywords
Cellulose; Dissolving pulp; Hot water treatment; Kraft pulping; Viscose; Xylan
Funding
- Academy of Finland through the PURCELL project [275398]
- Academy of Finland (AKA) [275398, 275398] Funding Source: Academy of Finland (AKA)
Ask authors/readers for more resources
Hot water treatments (HWTs) of unbleached hardwood kraft pulps under various process conditions were conducted to extract the xylan and thus produce a high-purity cellulosic pulp that could be used in dissolving applications. Increasing treatment temperature up to 240 degrees C increased the removal of xylan over the degradation of cellulose in birch pulp, but this effect was minor at higher temperatures. Addition of acetic acid lowered the treatment intensity needed to reach a certain degree of pulp purity, but did not improve the selectivity in xylan removal compared to water-only experiments. HWTs of eucalyptus pulp, with lower xylan content than birch pulp, produced cellulosic fibers with higher degree of polymerization at a given pulp purity. Under selected operational conditions (240 degrees C for 10 min) in a flow-through reactor, and provided that the HWTs were applied before bleaching, the chemical and macromolecular properties of water-treated pulps may be suitable for their conversion to viscose. Moreover, at high flow rates (200-400 mL/min), the extracted xylan was recovered from the aqueous hydrolysate in high yield and with relatively high molar mass (similar to 10 kDa). Based on the results of this study, HWTs of hardwood kraft pulp are suggested as a simple and green method to produce high-purity cellulose and polymeric xylan for high value-added applications.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available