Prussian blue analogue derived magnetic carbon/cobalt/iron nanocomposite as an efficient and recyclable catalyst for activation of peroxymonosulfate

A Prussian blue analogue, cobalt hexacyanoferrate Co-3[Fe(CN)(6)](2), was used for the first time to prepare a magnetic carbon/cobalt/iron (MCCI) nanocomposite via one-step carbonization of Co-3[Fe(CN)(6)](2). The resulting MCCI consisted of evenly-distributed cobalt and cobalt ferrite in a porous carbonaceous matrix, making it an attractive magnetic heterogeneous catalyst for activating peroxymonosulfate (PMS). As Rhodamine B (RhB) degradation was adopted as a model test for evaluating activation capability of MCCI, factors influencing RhB degradation were thoroughly examined, including MCCI and PMS dosages, temperature, pH, salt and radical scavengers. A higher MCCI dosage noticeably facilitated the degradation kinetics, whereas insufficient PMS dosage led to ineffective degradation. RhB degradation by MCCI-activated PMS was much more favorable at high temperatures and under neutral conditions. The presence of high concentration of salt slightly interfered with RhB degradation by MCCI-activated PMS. Through examining effects of radical scavengers, RhB degradation by MCCI-activated PMS can be primarily attributed to sulfate radicals instead of a combination of sulfate and hydroxyl radicals. Compared to Co3O4, a typical catalyst for PMS activation, MCCI also exhibited a higher catalytic activity for activating PMS. In addition, MCCI was proven as a durable and recyclable catalyst for activating PMS over multiple cycles without efficiency loss and significant changes of chemical characteristics. These features demonstrate that MCCI, simply prepared from a one-step carbonization of Co-3[Fe(CN)(6)](2), is a promising heterogeneous catalyst for activating PMS to degrade organic pollutants. (C) 2016 Published by Elsevier Ltd.