A novel La-containing additive for the long-term thermal stabilization of poly(vinyl chloride)

A new thermal stabilizer, La-Gly (Gly = n-[2-hydroxy-1,1-bis(hydroxymethyl)ethyl]-glycin), was synthesized. Through discoloration and dehydrochlorination tests at 180 degrees C, La-Gly is found to possess high stabilizing efficiency for poly(vinyl chloride) (PVC): as the mass ratio of La-Gly to PVC resin is increased from 0.3/50.0 to 2.0/50.0, the time to degradation of PVC samples increases from 90 min to 190 min. Studies on combinations of La-Gly and ZnSt(2), and of La-Gly and dibenzoyl methane (DBM) show that the initial color of PVC is improved, as the ratio of ZnSt(2) to La-Gly or DBM to La-Gly is increased from 0.3/1.2 to 1.2/03. One sample (50.0 g PVC, 0.6 g ZnSt2, 0.9 g La-Gly, 3.4 g tributyl citrate) shows the best balance between initial color and long-term thermal stability (140 min). Studies on dynamic thermal stability of the samples (50.0 g PVC, x g La-Gly, 3.4 g tributyl citrate, x = 0.3, 0.6, 0.9, 1.2, 1.5, 2.0) show that when x equals 1.2, the thermal dynamic stability time is 24.5 min, much longer than 6.4 min and 4.8 min, respectively, for two controls (50.0 g PVC, 1.5 g LaSt(3), 3.4 g tributyl citrate; 50.0 g PVC, 0.6 g CaSt(2), 0.9 g ZnSt(2), 3.4 g tributyl citrate). (C) 2017 Elsevier Ltd. All rights reserved.