Photoelectrochemical Performance of TiO2/Ti Electrode for Organic Compounds

Photoelectrochemical performance of TiO2/Ti electrode was investigated by using organic compounds. The TiO2/Ti electrode was prepared by anodic oxidation at a potential bias of 25 V for 4 h then calcined for 450 degrees C to obtain the anatase polymorph. Subsequently, it was characterized by X-Ray Diffraction (XRD) and Scanning Electron Microscope-Energy Dispersive X-ray (SEM-EDX). The XRD pattern showed that TiO2 has anatase phase as confirmed by 2 theta peaks at 37.93 degrees; 63.00 degrees, and 83.00 degrees. Using SEM-EDX data the TiO2 layer was formed on Ti plate with the composition of Ti (4.5 keV) and O (0.5 keV) elements. Furthermore, the photoelectrochemical sensing on the three organic compounds (ascorbic acid, glucose, and titan yellow) with the electrolyte addition showed that the linearity of TiO2/Ti electrode were 0.937, 0.968, and 0.938, meanwhile without the electrolyte were 0.998, 0.989, and 0.923, respectively.