ENGINEERING FAILURE ANALYSIS
Volume 58, Issue -, Pages 407-416Publisher
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.engfailanal.2015.05.022
Keywords
Rails; Flash butt welding; Fatigue cracking
Ask authors/readers for more resources
Medium carbon steel rails are commonly jointed by flash butt welding procedures. To ensure an adequate service life for the structural component, commonly subjected to fatigue loading, a rigorous quality control should be performed, both in welding parameters and in the surface quality of the welded joint. This work investigated the causes of recurrent failures in railroads, with cracking always initiated in the rail in the region of the welded joint. Two case studies are presented. Aiming to execute the failure analysis, all standard procedures were applied, with a careful assessment of the material characteristics and the fractured surface. It was concluded that, for both cases, fatigue cracks initiated near the weld bead and spread in a brittle mode, leading to premature fracture of the material. An in-depth analysis of the rails showed that the surface finishing of the weld bead was not appropriate, generating undesirable stress concentration. Some undesirable microstructural characteristics were also found in the weld region. A recommendation to control welding parameters and to change the procedure of surface finishing of welded joints was held, aiming to decrease the number of accidents on the railroads. (C) 2015 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available