Journal
ACS APPLIED ENERGY MATERIALS
Volume 2, Issue 3, Pages 1734-1746Publisher
AMER CHEMICAL SOC
DOI: 10.1021/acsaem.8b01850
Keywords
composite electrolyte; garnet; PEO; lithium metal; solid electrolyte; interface; lithium dendrite; solid-state NMR; elastic modulus; solid-state battery
Funding
- Gobierno Vasco [15, 18]
- MINECO [ENE2015-64907-C2-1-R]
- IKERBASQUE
Ask authors/readers for more resources
Ceramic-polymer solid electrolytes, combined with Li metal anodes, hold the promise for safer and more energetically dense battery technologies, as long as key interfacial challenges are fully understood and solved. Here, we investigate a garnet-PEO(LiTFSI) composite electrolyte system, the garnet filler being Li6.55Ga0.15La3Zr2O12 (LLZO) microparticles. A soft mechanical milling process ensures good miscibility between the garnet and polymer phases over a wide range of volume fraction (up to 70 vol % garnet). Excellent degree of structural and chemical homogeneity is achieved without degradation nor segregation, even at the local level, as confirmed by solid-state NMR spectroscopy, electron microscopy and gel permeation chromatography. The total Li-ion conductivity of the composites is governed by the polymer matrix, as a consequence of the high interfacial resistance (similar to 10(4) Omega cm(2)) between the garnet particles and the PEO(LiTFSI) matrix. However, by using Li-7 NMR 2D exchange spectroscopy (ESXY) in the solid state, it is shown that Li ions can locally exchange between the garnet surfaces to the surrounding polymer chains. This dynamic transfer phenomenon, occurring within the composite, seems to play a key role in kinetically stabilizing the interface with Li metal electrode, as observed from galvanostatic cycling and EIS experiments. Comparison of a garnet-free PEO electrolyte with a PEO-garnet (10 vol %) composite shows key performance improvements in the latter: although the Li-ion conductivity at 70 degrees C slightly decreases from 7.0 x 10(-4) S cm(-1), for PEO-LiTFSI, to 4.5 x 10(-4) S cm(-1) for 10 vol % LLZO, the composite shows up to 1 order of magnitude lower interfacial resistance with Li metal electrode (33 vs 300 Omega cm(2)), stable Li electrodeposition, and no dendrite formation. In contrast to previously believed, it is demonstrated that these improvements are not related to a change of the mechanical behavior but rather to a structural reorganization in the composite followed by local ion dynamics effects at the vicinity of the Li metal interface.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available