JOURNAL OF MATERIALS CHEMISTRY B
Volume 7, Issue 46, Pages 7415-7427Publisher
ROYAL SOC CHEMISTRY
DOI: 10.1039/c9tb01715a
Keywords
-
Categories
Funding
- Nature Science Foundation of China [81530050]
- Shaanxi Key Scientific and Technological Innovation Team [2017KCT-32]
Ask authors/readers for more resources
Although titanium implants have been applied in dental clinics to replace lost teeth and to restore masticatory function for decades, strategies to design the surface of the transmucosal sites of implants to achieve ideal and predictable biological sealing following implantation remain to be optimized. In this study, we hypothesized that gingival epithelial cell (GEC) adhesion and new tissue attachment to titanium sheets/implants could be promoted by the release of plasmid pLAMA3-CM (encoding a motif of the C-terminal globular domain of LAMA3) from a titanium surface. To test this hypothesis, a chitosan/collagen (Chi/Col) coating was immobilized on the surfaces of titanium substrates with nanotube topography (NT-Ti) through cathodic electrophoretic deposition; it was found that pLAMA3-CM could be released from the coating in a highly sustained manner. After culturing on titanium with nanotube topography coated by Chi/Col with the plasmid pLAMA3-CM (Chi/Col/pLAMA3-CM-Ti), human GECs (hGECs) were found to effectively uptake the incorporated plasmids, which resulted in improved attachment, as evidenced by morphological and immunofluorescence analyses. In addition, Chi/Col/pLAMA3-CM-Ti induced better biological sealing at transmucosal sites following immediate implantation into Sprague-Dawley rats. Our findings indicate that the modification of titanium implants by plasmid-mediated pLAMA3-CM gene transfection points to a practical strategy for optimizing biological sealing around the transmucosal sites of implants.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available