Influence of Temperature on Cyclic Fatigue Resistance of ProTaper Gold and ProTaper Universal Rotary Files

Introduction: The aim of this study was to evaluate the cyclic fatigue resistance of ProTaper Universal (PTU; Dentsply Maillefer, Baillagues, Switzerland) and Pro Taper Gold (PTG, Dentsply Maillefer) nickel-titanium rotary files at room and intracanal temperatures. Methods: A total of 120 files were used to test the cyclic fatigue resistance of PTU (S1 and F2) and PTG (S1 and F2) in an artificial canal at room temperature (20 degrees C) and at intracanal temperature (35 degrees C). The number of cycles to failure and the fracture length of the fragment were recorded, and data were subjected to statistical analysis. Results: PTG registered no differences in fatigue life between the 2 temperatures tested (P >.05), whereas PTU showed a statistically significant reduction in fatigue life at intracanal temperature compared with room temperature (P <.05). PTG instruments exhibited a statistically higher resistance to cyclic fatigue than PTU instruments both at room and intracanal temperatures (P <.05). There were no statistically significant differences among the fracture length of separated instruments (P >.05). Conclusions: Intracanal temperature influenced the cyclic fatigue resistance of instruments produced with traditional nickel titanium, whereas it did not influence the fatigue life of instruments produced with gold heat treatment. Gold heating treatment enhances the resistance to cyclic fatigue of ProTaper instruments.