Nano cellulose; in vivo study; Composite films; Curcumin; Silver nano particles
Ask authors/readers for more resources
With an aim to develop chitosan film with controllable swelling behavior and maximum antimicrobial efficacy, we hereby report cellulose nano crystals loaded chitosan films with Curcumin/Ag nano particles embedded as strong antimicrobial agents. The CNC had average size of 40-90 nm with poly dispersity index of 3.641. The TEM analysis of Ag NPs, produced via DMF reduction, revealed a particle size range of 15-25 nm. The Surface Plasmon resonance (SPR) of these Ag NPs shifted from 380 to 440 nm, with the increase in concentration of Ag (I). The TGA of the film samples Ch/CNC, and Ch/CNC (Ag-463/Cur(450)) exhibited% weight loss of around 95 and 80 respectively, thus indicating higher stability due to presence of Ag NPs. In XRD analysis 2 theta reflections at 38.12, 44.28 and 66.46 degrees confirmed the presence planes (1 1), (2 0) and (2 0) respectively. In skin irritation test, the mean Erythema scores observed after 72 h was zero for both the Curcumin and Ag NPs/Curcumin loaded films. The percent wound reduction, observed for the film samples Ch/CNC (Cur(450)) and Ch/CNC (Ag NP463/Cur(450)) was 57.8 and 97.2 respectively, indicating better suitability of Ag NPs/Curcumin loaded film. (C) 2017 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available