Journal
RSC ADVANCES
Volume 10, Issue 54, Pages 32885-32896Publisher
ROYAL SOC CHEMISTRY
DOI: 10.1039/d0ra04715e
Keywords
-
Categories
Funding
- National Nanoscience Postgraduate Teaching and Training Platform
- NRF
- UFS
- Sasol
Ask authors/readers for more resources
Graphene oxide (GO) was synthesisedviathe oxidation of graphite and was characterised using ATR FTIR, PXRD, SEM, TEM and TGA. These techniques confirmed the presence of characteristic oxygen-containing functional groups and the resulting increase in interlayer spacing in the nanostructure. GO is used as the support to form nanocomposites composed of combinations of the following: iron oxide nanoparticles (Fe3O4), carbon nanotubes (CNT) and palladium nanoparticles (Pd). The four final nanocomposites formed are: Pd/GO, Pd/Fe3O4/GO, Pd/CNT/GO, and Pd/CNT/Fe3O4/GO. Key intermediates were analysed using ATR FTIR for the confirmation of the modification. Additionally, all composites and their precursors underwent electron microscopic analysis to visually assess composite morphologies and the size distribution of deposited nanoparticles. The Fe(3)O(4)and Pd nanoparticles were indistinguishable from each other in their spherical shape and particle diameters, which were no bigger than 32 nm. From the TGA, incorporation of Fe3O4, CNT and finally Pd into the nanocomposites increased total thermal stability in terms of mass percentage lost over the temperature programme. GO showed significant decomposition, with all nanocomposites remaining relatively stable up to 120 degrees C. ICP OES results showed total Pd content by mass percentage for each final composite, varied from 7.9% to 9.1% mass Pd/collective mass. XPS confirmed the expected elemental compositions of composites according to their structures and the Pd-0 : Pd(II)ratios are obtained. The nanocomposites were tested for the catalytic reduction of nitrophenols. Pd/CNT/Fe3O4/GO gave the highest TOF ' for the reduction of 4-NP and 2-NP. For the reduction of 3-NP, Pd/GO showed the highest TOF '. Nitrophenol's pK(a)and catalyst TOF ' correlated in a direct proportional relationship for Pd/GO and Pd/Fe3O4/GO. It was found that Pd(0)surpassed Pd(II)in catalytic activity. Reduction of Pd(II)to Pd(0)took place during the first catalytic cycle.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available