Microwave-assisted reduction roasting-magnetic separation studies of two mineralogically different low-grade iron ores

The microwave-assisted reduction behaviours of two low-grade iron ores having a similar Fe content of 49wt% but distinctly different mineralogical and liberation characteristics were studied. Their performances in terms of the iron grade and recovery as obtained from statistically designed microwave (MW) roasting followed by low-intensity magnetic separation (LIMS) experiments were compared. At respective optimum conditions, the titano-magnetite ore (O1) could yield an iron concentrate of 62.57% Fe grade and 60.01% Fe recovery, while the goethitic ore (O2) could be upgraded to a concentrate of 64.4% Fe grade and 33.3% Fe recovery. Compared with the goethitic ore, the titano-magnetite ore responded better to MW heating. The characterization studies of the feed and roasted products obtained at different power and time conditions using X-ray diffraction, optical microscopy, vibrating-sample magnetometry, and electron-probe microanalysis explain the sequential reduction in the iron oxide phases. Finally, taking advantage of the MW absorbing character of the titano-magnetite ore, a blend of the same with the goethite-rich ore at a weight ratio of 60:40 (O2: O1) was subjected to MW roasting that resulted in a concentrate of 61.57% Fe grade with a Fe recovery of 64.47%.