Novel Mn-Ni spinel nanosheets were investigated for the NH3-SCR of NO at low temperature by ureahydrolysis (UH) and urea-hydrolysis hydrothermal-synthesis (UHHS), and compared with co-precipitation hydrothermal synthesis (CPHS) and co-precipitation (CP) methods. The optimum molar ratio of Mn/Ni (2 : 1) and urea/(Mn + Ni) (3 : 1) were determined, as also were the suitable hydrothermal temperature (130 degrees C for 24 h) and further calcination (450 degrees C for 6 h). An Mn(2)Ni(1)Ox-UHHS catalyst produced a purer spinelstructured NiMn2O4 nanosheet than Mn(2)Ni(1)Ox-UH, both of which showed highly efficient SCR activity (>98% NOx conversion at 100-250 degrees C) and N-2 selectivity (>95% at <150 degrees C and >85% at <250 degrees C). The NiMn2O4-UHHS nanosheet also exhibited excellent resistance to H2O and SO2 in the low-temperature range (85-90% NOx conversion at 150-300 degrees C with 10 vol% H2O and 150 ppm SO2). Characterization with BET, TPD, TPR, XPS SEM-EDS, TGA, AXNES and DRIFTS indicated that the main reasons for the excellent activity and resistances were the high specific surface area, greater NH3 adsorption ability and more efficient electronic interaction (Mn3+ + Ni3+ <-> Mn4+ + Ni2+) of active octahedral-sites in the [Ni2+Mn4+](tet)[Ni2+Ni3+Mn3+Mn4+](oct)O-4 spinel structure with an outside configuration of tetrahedrons embedded with Ni which avoided the sulfation of the inside octahedron-wrapped Mn active sites, and the nanosheet morphology which retarded the adhesion of sulfur ammonia species, resulting in the remission of deposition/inhibition effects. The reaction pathways were based on ER mechanisms via gaseous NO with adsorbed NH3-species and also the LH-then-ER mechanisms through the combination of bidentate nitrate with coordinated NH3/NH4+, which were less affected by SO2 competitive adsorption, attributed to be a major reason for good SO2-resistance.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available