Effect of Evening Primrose (Oenothera biennis) Oil Cake on the Properties of Polyurethane/Polyisocyanurate Bio-Composites

Rigid polyurethane/polyisocyanurate (RPU/PIR) foam formulations were modified by evening primrose (Oenothera biennis) oil cake as a bio-filler in the amount of 5 to 50 wt.%. The obtained foams were tested in terms of processing parameters, cellular structure (SEM analysis), physico-mechanical properties (apparent density, compressive strength, brittleness, accelerated aging tests), thermal insulation properties (thermal conductivity coefficient, closed cells content, absorbability and water absorption), flammability, smoke emission, and thermal properties. The obtained results showed that the amount of bio-filler had a significant influence on the morphology of the modified foams. Thorough mixing of the polyurethane premix allowed better homogenization of the bio-filler in the polyurethane matrix, resulting in a regular cellular structure. This resulted in an improvement in the physico-mechanical and thermal insulation properties as well as a reduction in the flammability of the obtained materials. This research provided important information on the management of the waste product from the edible oil industry and the production process of fire-safe RPU/PIR foams with improved performance properties. Due to these beneficial effects, it was found that the use of evening primrose oil cake as a bio-filler for RPU/PIR foams opens a new way of waste management to obtain new green materials.

Automated summary

The use of evening primrose oil cake as a bio-filler significantly influences the morphology of foams, leading to improved physico-mechanical and thermal insulation properties while reducing flammability. Thorough mixing allows better homogenization of the bio-filler in the polyurethane matrix, resulting in a regular cellular structure.