Keywords
Ce,Y:SrHfO3 ceramics; hot isostatic pressing; microstructure; grain refinement; scintillation properties
Categories
Funding
- National Key R&D Program of China [2017YFB0310500]
- National Natural Science Foundation of China [61775226]
- CAS President's International Fellowship Initiative [E00YGH21]
- European Structural and Investment Funds
- Czech Ministry of Education, Youth and Sports [SOLID21 CZ.02.1.01/0.0/0.0/16_019/0000760]
Ask authors/readers for more resources
Ce,Y:SrHfO3 ceramics were prepared by different methods in this study, and ceramics with good optical transparency were obtained using a two-step sintering method. The influence of pre-sintering temperature on the density, microstructure, and optical transparency of Ce,Y:SrHfO3 ceramics was studied under vacuum conditions.
Ce:SrHfO3 ceramics possess a strong stopping power to high-energy rays due to their high density and high effective atomic number. However, it is difficult to obtain transparent Ce:SrHfO3 ceramics via traditional sintering method because of its orthogonal structure. In this work, Ce, Y:SrHfO3 ceramics were prepared by long- time vacuum sintering and short-time vacuum pre-sintering combined with hot isostatic pressing (HIP). The Ce,Y:SrHfO3 powders with a pure phase and a mean particle size of 152 nm were prepared by calcining at 1200. for 8 h using metal oxides and carbonates. The Ce,Y:SrHfO3 ceramics vacuum-sintered at 1800. for 20 h are opaque with an average grain size of 28.6 mu m, while those prepared by the two-step sintering method show good optical transmittance. The evolution of the microstructure in the process of densification was analyzed in detail, and the influence of the pre-sintering temperature on the density, microstructure and optical transparency of Ce,Y:SrHfO3 ceramics was studied. The Ce,Y:SrHfO3 ceramics pre-sintered at 1500. for 2 h with HIP post-treatment at 1800. for 3 h have the highest in-line transmittance of 21.6% at 800 nm with a far smaller average grain size of 3.4 mu m. Under X-ray excitation, the Ce3+ 5d-4f emission of Ce,Y:SrHfO3 ceramics was observed at 400 nm, and the XEL integral intensity is 3.3 times higher than that of Bi4Ce3O12 (BGO) crystals. The light yield of the Ce,Y:SrHfO3 ceramics is approximately 3700 ph/MeV with the shaping time of 1 mu s. Good optical quality and scintillation performance of Ce,Y:SrHfO3 ceramics may expand the application range and potential in the field of scintillation detection.