A supramolecular polymer was developed by encapsulating polypyrrole in cucurbit[6]uril, improving the capacitor ability of conductive polypyrrole. The optimized ratio resulted in high specific capacitance and good cycling capacity. This study contributes to the improvement of supercapacitor performance.
A supramolecular polymer was developed through the encapsulation of polypyrrole by cucurbit[6]uril (PPy@Q[6]), which was employed as the electrode material to improve the capacitor ability of conductive polypyrrole. In the optimized ratio of 2 : 1 (C-PPy : C-Q[6]), the capacitor properties of the supramolecular material were evaluated, and a high specific capacitance of 414 F g(-1) at 10 mV s(-1) was obtained, which was 3.1 times higher than that of pure polypyrrole (132 F g(-1)). A comprehensive analysis suggested that the capacitance performances should be relevant to the component, surface area, and pore volume of the materials. The addition of 0.4 M Fe-2(SO4)(3) into the electrolyte provided a surprising specific capacitance of 3530 F g(-1) on the cucurbituril-encapsulated polypyrrole electrode material, with a high energy density of 707 W h kg(-1) at a power density of 32 000 W kg(-1) and a current density of 8 A g(-1). The 81.6% capacitance retention maintained after 1000 cycles revealed the acceptable cycling capacity of the proposed supramolecular supercapacitor system, which demonstrated good performance even at a low temperature of -20 degrees C.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available