The orange-emitting Ca5-x(PO4)(2)SiO4:xSm(3+) (C5PSO:Sm3+) phosphor was prepared via a simple solid-state method, and codoped with A(+) (A = Li, Na, and K) for improved luminescence performance. The effects of Sm3+ doping and Sm3+/A(+) codoping on the crystal structure and luminescence performance were investigated. A significant improvement in luminescence intensity was achieved through charge compensation of codoped A(+) ions.
The orange-emitting Ca5-x(PO4)(2)SiO4:xSm(3+) (C5PSO:Sm3+) phosphor was prepared via a simple solid-state method, and the charge compensators A(+) (A = Li, Na and K) were codoped into C5PSO:Sm3+ for improving the luminescence performance. The influences of Sm3+ doping and Sm3+/A(+) codoping on the crystal structure and the luminescence performance of the C5PSO:Sm3+ phosphor were investigated in detail. The X-ray diffraction results exhibited that all the as-prepared samples were assigned to the standard structure Ca-5(PO4)(2)SiO4 possessing the P63/m space group. Upon near-ultraviolet excitation at 401 nm, the characteristic emission peaks of the C5PSO:Sm3+ phosphors are located at 558 nm, 605 nm and 656 nm, respectively, which are derived from the (4)G(5/2) -> H-6(J) (J = 5/2, 7/2, and 9/2) electron transitions of Sm3+ ions. Furthermore, a significant luminescence improvement of the C5PSO:Sm3+ phosphor was attained through charge compensation of codoped A(+) ions, and the emission intensity is enhanced by 1.79-, 1.45-, and 1.14-fold for K+, Na+, and Li+, respectively. In addition, the actual orange-red LED and w-LED fabricated with the as-prepared C5PSO:Sm3+,K+ phosphor showed excellent optical performance. All the results demonstrated that the C5PSO:Sm3+,K+ orange-emitting phosphor could act as a potential orange-red component in the w-LEDs illumination field.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available