Temperature swing adsorption; Desiccant; Molecular sieve stability; Gas dehydration
Categories
Ask authors/readers for more resources
This study investigates the degradation rates of different materials during long-term cycling using a rapid cycling thermal swing adsorption apparatus. It is found that higher regeneration temperatures result in greater capacity loss for all tested materials. Interestingly, the inclusion of water in the regenerating gas stream mitigates the degradation of the desiccants.
Many raw and treated natural gas streams are dehydrated using temperature swing adsorption with molecular sieves. These systems are designed to operate for years at a time, with adsorbent materials subjected to thousands of cycles. Despite all the efforts in adsorption research, there is very little open literature on the degradation of these materials over prolonged cycling. In this work, we investigated the degradation rates of zeolite 4A, zeolite 13X and three different pore size silica gels using a rapid cycling thermal swing adsorption apparatus. Zeolite 13X was found to lose 31 %, 51 % and 68 % of its adsorption capacity after 5,000 temperature swing adsorption cycles at regeneration temperatures of T = 150, 200 and 250 degrees C, respectively. It is noted that all tested materials had a higher capacity loss at a higher regeneration temperature. At a regeneration temperature of T = 250 degrees C zeolite 4A, 22 ?, pore size silica, 30 ?, pore size silica and 60 ?, pore size silica were observed to lose 6 %, 52 %, 33 % and 19 % adsorption capacity, respectively, after 5,000 temperature swing adsorption cycles. Interestingly, all five materials showed lower degradation rates when water was included in the regenerating gas stream, indicating that a wet gas regeneration can mitigate the degradation of the desiccants.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available