Anchoring a Pt-based alloy on oxygen-vacancy-defected MXene nanosheets for efficient hydrogen evolution reaction and oxygen reduction reaction

Rational design and controllable synthesis of Pt-based materials with intimate interfacial contact open up the possibility for boosting the performance of the ORR (oxygen reduction reaction) and HER (hydrogen evolution reaction). However, it is still challenging to prevent the oxidation of Pt during the formation of alloys and to clarify the interfacial synergistic effects on the catalytic performance between Pt alloys and the dispersed substrate. Herein, the wet chemical stripping and intercalation methods were employed to synthesize a two-dimensional (2D) MXene with abundant defect sites, which can anchor Pt3Co/Pt3Ni nanoparticles and prevent the oxidation of Pt during the process of atomic rearrangement at high temperatures. The obtained Pt3Co/MXene and Pt3Ni/MXene displayed different phase compositions and alloying degrees on adjusting the annealing temperature. Electrochemical test results showed that the optimized HER and ORR electrocatalytic activities occurred at 700 degrees C. Compared with Pt3Ni/MXene-700, Pt3Co/MXene-700 exhibited an HER overpotential of 1.3 mV at a current density of 10 mA cm-2, and a Tafel slope of 27.11 mV dec-1 in 0.1 M HClO4 solution. Furthermore, Pt3Co/MXene-700 exhibited an ORR half-wave potential of 0.897 V, and a mass activity of 241.1 mA mg-1Pt in 0.1 M HClO4 solution. This can be attributed to the formation of intermetallic compounds in Pt3Co/MXene. The electronic structure analysis showed that the enhanced performance could be assigned to the electron-capturing capability of the MXene, less oxidation of Pt and synergistic interactions between the Pt alloy and the MXene substrate. These findings provide a new strategy for the synthesis of highly active HER/ORR catalysts and broaden the way for the design of MXene-based catalysts. Two-dimensional MXenes enriched with oxygen vacancy defects can anchor Pt-based alloys to facilitate the hydrogen evolution reaction and oxygen reduction reaction.

Automated summary

The synthesis of Pt-based alloys anchored on MXene with oxygen vacancy defects demonstrates enhanced catalytic performances for the hydrogen evolution reaction (HER) and oxygen reduction reaction (ORR). By utilizing wet chemical stripping and intercalation methods, the oxidation of Pt during the formation of alloys is prevented, and the interfacial synergistic effects between Pt alloys and the dispersed substrate are clarified. The optimized catalytic activities for HER and ORR are achieved at 700 degrees C. These findings provide new insights into the design of highly active catalysts and broaden the application of MXene-based catalysts.