Journal
ACTA MATERIALIA
Volume 263, Issue -, Pages -Publisher
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.actamat.2023.119530
Keywords
Magnetocaloric effect; Magnetostructural transition; Ferromagnetic martensitic transformation; MM'X alloys
Ask authors/readers for more resources
This study reports a significant improvement in the reversibility and mechanical stability of MnNiGe-based alloys through grain orientation. The oriented grains allow for synergistic deformations during the magnetostructural transition, reducing stress concentration. The textured alloys also exhibit low thermal hysteresis and a large reversible isothermal entropy change, making them attractive for practical applications.
Materials that undergo a magnetostructural transition (MST) usually exhibit fascinating magnetoresponsive properties, making them an important class of smart materials. However, practical application of this class of smart materials has been hindered by structural degradation as well as large irreversibility of the MST during consecutive thermal and field cycles. Here we report a significant improvement of the reversibility and mechanical stability in grain-oriented MnNiGe-based alloys that were fabricated using a directional solidification method. The preferred grain orientation enables synergistic deformations between neighboring grains during the MST, leading to a substantial reduction in the transition-induced stress concentration. As a result, in situ and ex situ microscopic observations demonstrate a good mechanical stability of the textured alloys across the MST, in strong contrast to conventional MM'X (M, M' = Mn, Fe, Co, Ni; X = Si, Ge) materials with randomly-oriented grains. The detailed transition stages of the MST have also been observed at the microscopic scale, and are reported for the first time in the MM'X family. Besides, a low thermal hysteresis (Delta T-hys) of similar to 4 K was obtained in the textured alloys, which is the lowest Delta T-hys in the MM'X material family. Textured MnNiGe-based alloys show a large reversible isothermal entropy change (>= 35.9 Jkg(-1)K(-1)) in a 5 T field change, which is the highest among typical magnetocaloric materials. Consequently, this work provides a promising strategy for enhancing the cyclic stability of materials with a MST, which may boost their practical applications in solid-state refrigerators, energy harvesters and high-precision actuators.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available