LARP-assisted synthesis of CsBi3I10 perovskite for efficient lead-free solar cells

Bismuth-based perovskites are an important class of materials in the fabrication of lead-free perovskite solar cells. Bi-based Cs3Bi2I9 and CsBi3I10 perovskites are getting much attention due to their appropriate bandgap values of 2.05 eV and 1.77 eV, respectively. However, the device optimisation process plays a key role in controlling the film quality and the performance of perovskite solar cells. Hence, a new strategy to improve crystallization as well as the thin film quality is equally important to develop efficient perovskite solar cells. Herein, an attempt was made to prepare the Bi-based Cs3Bi2I9 and CsBi3I10 perovskites via the ligand-assisted re-precipitation approach (LARP). The physical, structural, and optical properties were investigated on perovskite films deposited by the solution process for solar cell applications. Cs3Bi2I9 and CsBi3I10-based perovskite-based solar cells were fabricated using the device architecture of ITO/NiOx/perovskite layer/PC61BM/BCP/Ag. The device fabricated with CsBi3I10 showed the best power conversion efficiency (PCE) of 2.3% with an improved fill factor (FF) of 69%, V-OC of 0.79 V, and J(SC) of 4.2 mA cm(-2) compared to the Cs3Bi2I9-based device which showed a PCE of 0.7% with a FF of 47%, V-OC of 0.62 V and J(SC) of 2.4 mA cm(-2).

Automated summary

Bismuth-based perovskites are important materials in lead-free perovskite solar cells. A new strategy of ligand-assisted re-precipitation approach is used to improve crystallization and thin film quality. CsBi3I10-based perovskite solar cells show the highest power conversion efficiency of 2.3%.