Journal
SCIENTIFIC REPORTS
Volume 6, Issue -, Pages -Publisher
NATURE PUBLISHING GROUP
DOI: 10.1038/srep23183
Keywords
-
Categories
Funding
- Basic Science Research Programs through the National Research Foundation of Korea (NRF) - Ministry of Education, Science and Technology [2012R1A6A3A04038530]
- Korea Ministry of Environment (MOE) as Public Technology Program based on Environmental policy [2014000160001]
- National Research Foundation of Korea [2012R1A6A3A04038530, 22A20153913497] Funding Source: Korea Institute of Science & Technology Information (KISTI), National Science & Technology Information Service (NTIS)
Ask authors/readers for more resources
For ex-situ co-doping methods, sintering at high temperatures enables rapid diffusion of Sn4+ and Be2+ dopants into hematite (alpha-Fe2O3) lattices, without altering the nanorod morphology or damaging their crystallinity. Sn/Be co-doping results in a remarkable enhancement in photocurrent (1.7 mA/cm(2)) compared to pristine alpha-Fe2O3 (0.7 mA/cm(2)), and Sn4+ mono-doped alpha-Fe2O3 photoanodes (1.0 mA/cm(2)). From first-principles calculations, we found that Sn4+ doping induced a shallow donor level below the conduction band minimum, which does not contribute to increase electrical conductivity and photocurrent because of its localized nature. Additionally, Sn4+-doping induce local micro-strain and a decreased Fe-O bond ordering. When Be2+ was co-doped with Sn4+-doped alpha-Fe2O3 photoanodes, the conduction band recovered its original state, without localized impurities peaks, also a reduction in micro-strain and increased Fe-O bond ordering is observed. Also the sequence in which the ex-situ co-doping is carried out is very crucial, as Be/Sn co-doping sequence induces many under-coordinated O atoms resulting in a higher micro-strain and lower charge separation efficiency resulting undesired electron recombination. Here, we perform a detailed systematic characterization using XRD, FESEM, XPS and comprehensive electrochemical and photoelectrochemical studies, along with sophisticated synchrotron diffraction studies and extended X-ray absorption fine structure.