Journal
MATERIALS LETTERS
Volume 352, Issue -, Pages -Publisher
ELSEVIER
DOI: 10.1016/j.matlet.2023.135129
Keywords
Metals and alloys; Microstructure; Mechanical properties; Stacking faults; Fracture
Ask authors/readers for more resources
The effect of Ti and Sr on the microstructure and mechanical properties of Al-Si-Cu-Ni alloy was investigated. It was found that the addition of 0.1% Ti and 0.02% Sr led to a significant reduction in grain size and a change in the morphology of eutectic Si. Sr promoted the formation of stacking faults and nano-Al2Cu. The ultimate tensile strength, yield strength, and elongation were greatly increased, reaching 239.6 MPa, 140.6 MPa, and 2.11% respectively.
The effect of Ti and Sr on the microstructure and mechanical properties of Al-Si-Cu-Ni alloy was studied. Research showd that the addition of 0.1% Ti and 0.02% Sr significantly reduced grain size and changed the morphology of eutectic Si. Sr promoted the formation of stacking faults and nano-Al2Cu. The strength and plasticity were significantly increased with ultimate tensile strength, yield strength and elongation being 239.6 MPa, 140.6 MPa, and 2.11%, respectively.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available