Low temperature deposition of a-SiC:H thin films applying a dual plasma source process

The utilization of silicon carbide (SiC) thin films is of great interest whenever a high robustness is requested for MEMS/NEMS-based devices, which are operated in harsh environments beyond the applicability of standard silicon technology. Hydrogenated amorphous SiC (a-SiC:H) is especially attractive for these scenarios, as it can be deposited at temperatures lower than 400 degrees C while still being beneficial for enhanced device performance. Furthermore, the thin film properties can be tailored to a great extent during synthesis or via post-deposition annealing. This study reports on the deposition of a-SiC:H thin films at a substrate temperature of 250 degrees C applying a dual plasma process by superimposing a radio frequency (RF) plasma which excites the substrate table to an inductively-coupled RF plasma. This auxiliary plasma source has a huge impact on the resulting thin film properties due to the interaction of various opposing processes during film growth. To understand these processes, the layer composition was determined using time-of-flight elastic recoil detection analyses, Fourier transform infrared spectroscopy and by mass effusion measurements up to 1000 degrees C, thus revealing changes in chemical composition, but also the power dependent incorporation of gaseous species from the plasma. This, for example, allows modification of the residual stress ranging from nearly stress free to highly compressively stressed layers of more than -2 GPa, Young's modulus values ranging from about 168 GPa down to 48 GPa, but also greatly affects the surface topography which can be adjusted to a very low root mean squared roughness of less than 0.1 nm. (C) 2016 Elsevier B.V. All rights reserved.