Journal
SURFACE ENGINEERING
Volume 33, Issue 1, Pages 56-62Publisher
TAYLOR & FRANCIS LTD
DOI: 10.1080/02670844.2016.1176718
Keywords
Fe-based amorphous coating; Corrosion resistance; Wear resistance; Thermal spraying
Categories
Funding
- National Natural Science Foundation of China [51501210, 51571207]
- Ningbo Municipal Nature Science Foundation [2015A610002]
Ask authors/readers for more resources
The amorphous coating with a new developed composition of Fe63Cr8Mo3.5Ni5P10B4C4Si2.5 has been successfully prepared by high velocity oxygen fuel technique. The amorphous coating shows good corrosion and wear resistance, which compare favourably with those of the well-known SAM1651 (Fe48Mo14Cr15Y2C15B6) and SAM2X5 (Fe49.7Cr18Mn1.9Mo7.4W1.6B15.2C3.8Si2.4) amorphous coatings despite the absence of W, and very low Cr and Mo content. The electrochemical impedance spectroscopy (EIS) and Mott-Schottky analysis reveal that under high passive potentials the passive film on the coating reflects bi-layer structure and transpassive dissolution occurs, but the film can still remain passive due to slow ionic transport under these conditions. Donor densities of the passive films on the coatings are in the order of magnitude of 10(21)cm(-3) which is comparable to the reported values for passive films of SAM series amorphous coatings indicating the approximate stability of the passive film. In addition, the dominating wear mechanism of Fe-based amorphous coatings is oxidation wear.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available