Novel hydrogel poly (GG-co-acrylic acid) for the sorptive removal of the color Rhodamine-B from contaminated water

Textile effluent's treatment is highly desired due to the presence of hazardous, water-soluble and non-biodegradable dyes that not only have harmful effect on the environment but on living beings as well. Treatment of these pollutants by sorption through biosorbents is considered to be a best method of choice due to greener nature of the processes. In this connection hydrogel sorbents might be an intriguing option due to its straightforward application, great efficacy, easy synthesis, rapid turnaround, and potential of recycling. Herein, novel hydrogel was prepared using Gellan Gum and acrylic acid (GG-co-AAc) which were then characterized by instrumental techniques like UV/visible and FTIR spectroscopy, SEM, EDX and XRD. The anionic hydrogel's adsorption capacity, swelling behavior, and sorption potential were determined using Rhodamine-B as potential environmental pollutant. The hydrogel exhibited an impressive adsorption capacity of 1250 mg/g. Swelling experiments were performed in Milli-Q distilled water at different pH levels, reaching maximum swelling of 3230% after 23 h as determined through Fickian diffusion. At pH 7, the anionic hydrogel's sorption potential was thoroughly studied in the subsequent experiments. The adsorption process was found to follow the Langmuir isotherm, indicating a monolayer adsorption mechanism supported by higher R2 values compared to the Freundlich isotherm. Thermodynamic analysis revealed the exothermic nature of the adsorption process, with a negative enthalpy value of -11371 KJmol-1 and negative entropy value of -26.39 Jmol-1K-1, suggesting a less ordered system. These findings provide valuable insights into the adsorption characteristics and potential applications of the synthesized anionic hydrogel.

Automated summary

Treatment of textile effluent is important due to the presence of harmful and non-biodegradable dyes. Biosorption using hydrogel sorbents is a green and effective method. In this study, a novel hydrogel was synthesized and characterized. The hydrogel showed high adsorption capacity and swelling behavior, with excellent sorption potential at pH 7. Thermodynamic analysis indicated an exothermic nature of the adsorption process. These findings provide valuable insights into the characteristics and applications of the synthesized hydrogel.