Journal
SURFACES AND INTERFACES
Volume 40, Issue -, Pages -Publisher
ELSEVIER
DOI: 10.1016/j.surfin.2023.103076
Keywords
Interfacial analysis; Cu; SiO 2 hybrid bonding; Voids; 3D IC integration
Ask authors/readers for more resources
This paper presents a new plasma-free surface modification approach for low temperature Cu/SiO2 hybrid bonding using a 1-M KOH solution. The KOH solution makes the Cu surface more hydrophilic without increasing its roughness. The results show that the bonding temperature can be lowered to 200 degrees C while maintaining high bonding strength and reliability performance.
This paper reports a novel plasma-free surface modification approach for low temperature Cu/SiO2 hybrid bonding. A 1-M KOH solution was employed, which acts as a hydroxyl group supply and further modifies the surface of SiO2 dielectric layer by the Si-OH transformation. Such a KOH solution makes the Cu surface more hydrophilic without increasing its surface roughness. We found that the contact angles significantly decreased after dipping into 0.5-3 M of KOH. A contact angle below 5 degrees was achieved with > 1 M KOH. The X-ray photoelectron spectroscopy (XPS) results showed an increase in Si-OH (7.8% to 40.6%) and decreases in Si-O-Si (64% to 55%), Si-O and C-O (28.2% to 4.4%) intensities after KOH wet treatment. Furthermore, the KOH treatment almost does not etch nor roughen the Cu surfaces. Therefore, the bonding temperature could be lowered to 200 degrees C while keeping high bonding strength and reliability performance. A low specific contact resistance of 5 x 10-8 & omega;.cm2 was obtained. Results obtained by scanning electron microscope (SEM) and transmission electron microscope (TEM) show the excellent bonding quality of both SiO2-SiO2 and Cu-Cu interface. Additionally, energy-dispersive X-ray spectrometry (EDS) analyses show no signs of oxides and potassium contaminations at the bonding interfaces.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available