Keywords
Magnesium alloy; Coating; Plasma electrolytic oxidation; Discontinuous deposition; Wear resistance; Mechanism.
Categories
Ask authors/readers for more resources
A novel super wear-resistant coating for magnesium alloys was achieved by combining plasma electrolytic oxidation (PEO) and discontinuous sealing (DCS), resulting in a significant enhancement of wear resistance.
Magnesium alloys are lightweight materials with great potential, and plasma electrolytic oxidation (PEO) is effective surface treatment for necessary improvement of corrosion resistance of magnesium alloys. However, the similar to 14 mu m thick and rough PEO protection layer has inferior wear resistance, which limits magnesium alloys as sliding or reciprocating parts, where magnesium alloys have special advantages by their inherent damping and denoising properties and attractive light-weighting. Here a novel super wear-resistant coating for magnesium alloys was achieved, via the discontinuous sealing (DCS) of a 1.3 mu m thick polytetrafluoroethylene (PTFE) polymer layer with an initial area fraction (Af) of 70% on the necessary PEO protection layer by selective spraying, and the wear resistance was exceptionally enhanced by similar to 5500 times in comparison with the base PEO coating. The initial surface roughness (Sa) under PEO +DCS (1.54 mu m) was imperfectly 59% higher than that under PEO and conventional continuous sealing (CS). Interestingly, DCS was surprisingly 20 times superior for enhancing wear resistance in contrast to CS. DCS induced nano-cracks that splitted DCS layer into multilayer nano-blocks, and DCS also provided extra space for the movement of nano-blocks, which resulted in rolling friction and nano lubrication. Further, DCS promoted mixed wear of the PTFE polymer layer and the PEO coating, and the PTFE layer (HV: 6 Kg center dot mm -2, Af: 92.2%) and the PEO coating (HV: 310 Kg center dot mm -2, Af: 7.8%) served as the soft matrix and the hard point, respectively. Moreover, the dynamic decrease of Sa by 29% during wear also contributed to the super wear resistance. The strategy of depositing a low-frictional discontinuous layer on a rough and hard layer or matrix also opens a window for achieving super wear-resistant coatings in other materials. (c) 2023 Chongqing University. Publishing services provided by Elsevier B.V. on behalf of KeAi Communications Co. Ltd. This is an open access article under the CC BY-NC-ND license ( http://creativecommons.org/licenses/by-nc-nd/4.0/ ) Peer review under responsibility of Chongqing University
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available