Study on Sulfuric Acid Leaching and Purification of Zinc Ferrite by Roasting Zinc-Containing Gossan Ore

Gossan discarded from mining processes result in metal resource wastage, and its long-term stacking causes environmental hazards. Therefore, this article considers zinc-containing gossan as the research object. The ore was roasted to prepare primary zinc ferrite products and sulfuric acid leaching was performed for purification. Then, XRD analysis was performed to characterize the purified products. The results indicated that the effect of sulfuric acid concentration on the purification of the products was related to its zinc ferrite content. Furthermore, the effect of leaching temperature on the purification of zinc ferrite products was related to sulfuric acid concentration; the lower the sulfuric acid concentration, the more considerable the effect of leaching temperature. The conditions suitable for purifying the products through sulfuric acid leaching are as follows: sulfuric acid concentration of 140 g/L, liquid-solid ratio of 4:1, leaching temperature of 80 & DEG;C, leaching time of 120 min, and stirring speed of 300 rpm. This article determines the factors affecting the purification of zinc ferrite by sulfuric acid leaching along with the optimal purification conditions. The findings presented herein provide a theoretical foundation for the development of new processes for preparing zinc ferrite, which has considerable industrial application value.

Automated summary

Gossan discarded from mining processes causes metal resource wastage and environmental hazards. This study focuses on zinc-containing gossan and investigates its purification through sulfuric acid leaching. The study identifies the factors affecting the purification process and provides optimal conditions for purifying zinc ferrite, which has significant industrial application value.