Post-CMOS processing challenges and design developments of CMOS-MEMS microheaters for local CNT synthesis

Carbon nanotubes (CNTs) can be locally grown on custom-designed CMOS microheaters by a thermal chemical vapour deposition (CVD) process to utilize the sensing capabilities of CNTs in emerging micro- and nanotechnology applications. For such a direct CMOS-CNT integration, a key requirement is the development of necessary post-processing steps on CMOS chips for fabricating CMOS-MEMS polysilicon heaters that can locally generate the required CNT synthesis temperatures (similar to 650-900 degrees C). In our post-CMOS processing, a subtractive fabrication technique is used for micromachining the polysilicon heaters, where the passivation layers in CMOS are used as masks to protect the electronics. For dielectric etching, it is necessary to achieve high selectivity, uniform etching and a good etch rate to fully expose the polysilicon layers without causing damage. We achieved successful post-CMOS processing by developing two-step reactive ion etching (RIE) of the SiO2 dielectric layer and making design improvements to a second-generation CMOS chip. After the dry etching process, CMOS-MEMS microheaters are partially suspended by SiO2 wet etching with minimum damage to the exposed aluminium layers, to obtain high thermal isolation. The fabricated microheaters are then successfully utilized for synthesizing CNTs by a local thermal CVD process. The CMOS post-processing challenges and design aspects to fabricate CMOS-MEMS polysilicon microheaters for such high-temperature applications are detailed in this article. Our developed process for heterogeneous monolithic integration of CMOS-CNT shows promise for wafer-level manufacturing of CNT-based sensors by incorporating additional steps in an already existing foundry CMOS process.

Automated summary

Carbon nanotubes (CNTs) were successfully grown on custom-designed CMOS microheaters by a thermal chemical vapour deposition (CVD) process. A two-step reactive ion etching (RIE) method and design improvements were employed to achieve high selectivity, uniform etching, and a good etch rate. The CMOS-MEMS microheaters fabricated through this process were utilized for synthesizing CNTs by a local thermal CVD process.