Effect of recrystallization on bainite transformation and mechanical properties of complex phase steel with high formability (CH steel)

Journal

JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T
Volume 26, Issue -, Pages 7674-7693

Publisher

ELSEVIER
DOI: 10.1016/j.jmrt.2023.09.104

Keywords

Complex phase steel with high; formability (CH steel); Recrystallization; Bainite transformation; Microstructure; Mechanical properties

Ask authors/readers for more resources

The effect of recrystallization on bainite transformation and mechanical properties of CH steel was investigated. It was found that precipitation hindered recrystallization, while a lower degree of recrystallization promoted bainite transformation and improved mechanical properties. During annealing, the samples showed grain refinement, increased dislocation, and strengthening from precipitation, leading to enhanced strength.
Herein, the effect of recrystallization on the bainite transformation and mechanical properties of CH steel were investigated using SEM, TEM, EBSD, dilatometry, and tensile testing machine. First, precipitation was introduced to hinder recrystallization by batch annealing. Subsequently, the competitive relationship between austenite transformation and recrystallization was revealed using different annealing processes. Finally, the effect of recrystallization on bainite transformation was analyzed, mainly including bainite morphology, fraction, transformation rate, bainite nucleation rate of untransformed austenite and austenite-bainite orientation relationship, as well as the effect on the me-chanical properties. After batch annealing, a large amount of cementite and nanoscale (Nb, Ti)C precipitated in the hot-rolled sheet, the austenite transformation start temperature (Ac1) and the pearlite to austenite transformation end temperature (Ac1f)of the cold-rolled sheet increased, and the austenite transformation end temperature (Ac3) of the cold-rolled sheet decreased, and the austenite transformation process accelerated. The micro-structure of annealed sheets is consisted of ferrite, granular bainite, martensite, and a small fraction of retained austenite. Carbide hindered the recrystallization process during the annealing process, resulting in significant refining of the grains. The lower degree of recrystallization promoted bainite transformation, providing more nucleation sites, higher grain boundary and autocatalytic nucleation activation energy, improving bainite's fraction and transformation rate. The bainitic ferrite was mainly lathy in the recrystallized zone and polygonal in the non-recrystallized zone. Both a K-S and an N-W relationship between retained austenite and bainite, while the N-W relationship in the non-recrystallized zone was relatively higher. Without severe loss of plasticity, hindering recrystallization increased the dislocation, grain refinement, and precipitation strengthening values of the samples, and the strength significantly improved. However, with the increase of annealing temperature, recrystallization fraction increased gradually, and the increase in strength became less noticeable.(c) 2023 The Author(s). Published by Elsevier B.V. This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/).

Authors

I am an author on this paper
Click your name to claim this paper and add it to your profile.

Reviews

Primary Rating

4.7
Not enough ratings

Secondary Ratings

Novelty
-
Significance
-
Scientific rigor
-
Rate this paper

Recommended

No Data Available
No Data Available