Oligocarbonate diols; Carbon dioxide; Metal -free Lewis acid -base catalysts; Polycarbonate urethanes; Biodegradable polymer
Ask authors/readers for more resources
Oligocarbonate diols (PPCDL) with a high carbonate content were successfully synthesized through direct copolymerization of propylene oxide (PO) and carbon dioxide (CO2) using metal-free Lewis acid-base catalysts and 1,4-butanediol (BDO) as a proton exchange agent (PEA). The molar ratio of PO to BDO, temperature, pressure, and reaction time were investigated to control the molecular weight of the oligocarbonate diols. The structures of the diols were characterized by various analytical techniques, and their rheological properties were studied. Furthermore, polycarbonate urethanes were prepared using the synthesized PPCDLs and showed promising thermal and mechanical properties for polyurethane applications.
Oligocarbonate diols (PPCDL) with carbonate content higher than 90% were successfully synthesized by the direct copolymerization of propylene oxide (PO) and carbon dioxide (CO2) using metal-free Lewis acid-base catalysts in the presence of 1,4-butanediol (BDO) as proton exchange agent (PEA). The effects of molar ratio of PO to BDO, temperature, pressure and reaction time on the copolymerization were systematically investigated. The molecular weight of the prepared oligocarbonate diols is in good linear relationship to PO/BDO feeding ratio and can be easily and precisely controlled in the range of 1000-4000 g mol- 1. The detailed structures of the oligocarbonate diols were fully investigated by 1H NMR, 13C NMR, MALDI-TOF analysis. The rheological properties of synthesized PPCDL were also studied using a rheometer. Finally, polycarbonate urethanes were designed and successfully prepared using the PPCDLs as soft segment and 4,4 & PRIME;-diphenylmethane diisocyanate (MDI) and BDO as hard segment. The comprehensive evaluation of thermal and mechanical properties of the synthesized poly(carbonate urethane)s (PCUs) demonstrates their complete feasibility in the application of polyurethane industry.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available