Journal
SURFACE & COATINGS TECHNOLOGY
Volume 467, Issue -, Pages -Publisher
ELSEVIER SCIENCE SA
DOI: 10.1016/j.surfcoat.2023.129728
Keywords
Graphene oxide; Layered double hydroxide; Silane functionalization; Corrosion protection
Ask authors/readers for more resources
In this study, a modified LDH-MoO42- nano-filler (KGO@LM) was prepared by modifying KH-570 and GO to improve the long-term corrosion resistance of epoxy resin (EP) coating. The filler integrates the functions of barrier, chloride ion trapping, and self-repair, and has good dispersion and compatibility in EP. The addition of KGO@LM filler significantly improved the anticorrosive effect of EP coating, as evidenced by the high impedance and significant corrosion inhibiting effect.
Common coatings have unsatisfactory long-term anticorrosion performance due to poor barrier property. In this work, LDH-MoO42- nano-filler (KGO@LM) modified by KH-570 and GO was prepared to improve the long-term corrosion resistance of epoxy resin (EP) coating. The filler integrates the three functions of barrier, chloride ion trapping and self-repair, and has good dispersion and compatibility in EP. After soaking in 3.5 wt% NaCl solution for 28 days, the low-frequency impedance of KGO@LM coating was still as high as 1.02 x 10(8) Omega.cm(2), while the remaining value of EP coating was only 2.63 x 10(6) Omega cm(2),so the addition of KGO@LM filler significantly improved the anticorrosive effect of EP coating. After soaking in 3.5 wt% NaCl solution for 18 h, the lowfrequency impedance of the scratched KGO@LM/EP coating was 1.5 orders of magnitude higher than that of the EP coating, which proved that the designed filler had a significant corrosion inhibiting effect. Therefore, it is believed that this work can provide some inspirations for other researchers to develop long-term anticorrosion coatings.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available