Fast and Uncooled Semiconducting Ca-Doped Y-Ba-Cu-O Thin Film-Based Thermal Sensors for Infrared

YBa2Cu3O6+x (YBCO) cuprates are semiconductive when oxygen depleted (x < 0.5). They can be used for uncooled thermal detection in the near-infrared: (i) low temperature deposition on silicon substrates, leading to an amorphous phase (a-YBCO); (ii) pyroelectric properties exploited in thermal detectors offering both low noise and fast response above 1 MHz. However, a-YBCO films exhibit a small direct current (DC) electrical conductivity, with strong non-linearity of current-voltage plots. Calcium doping is well known for improving the transport properties of oxygen-rich YBCO films (x > 0.7). In this paper, we consider the performances of pyroelectric detectors made from calcium-doped (10 at. %) and undoped a-YBCO films. First, the surface microstructure, composition, and DC electrical properties of a-Y0.9Ca0.1Ba2Cu3O6+x films were investigated; then devices were tested at 850 nm wavelength and results were analyzed with an analytical model. A lower DC conductivity was measured for the calcium-doped material, which exhibited a slightly rougher surface, with copper-rich precipitates. The calcium-doped device exhibited a higher specific detectivity (D* = 7.5 x 10(7) cm.root Hz/ W at 100 kHz) than the undoped device. Moreover, a shorter thermal time constant (<8 ns) was inferred as compared to the undoped device and commercially available pyroelectric sensors, thus paving the way to significant improvements for fast infrared imaging applications.

Automated summary

This study investigates the performance of detectors made from calcium-doped and undoped a-YBCO films. The calcium-doped material shows lower DC conductivity and a slightly rougher surface compared to the undoped material. The calcium-doped device exhibits higher specific detectivity and shorter thermal time constant, suggesting significant improvements for fast infrared imaging applications.