JOURNAL OF NON-CRYSTALLINE SOLIDS
Volume 613, Issue -, Pages -Publisher
ELSEVIER
DOI: 10.1016/j.jnoncrysol.2023.122373
Keywords
Powder compact; Amorphous; Spark plasma sintering (SPS); Magnetic flux density ( B )
Ask authors/readers for more resources
Amorphous powder compacts of Fe77.7Si8B10P4Cu0.3 with high relative density (rho r = 94%), high saturated magnetic induction (Bs = 1.34 T), and high permeability (mu = 163 at 20 kHz) were fabricated by spark plasma sintering. Fe77.7Si8B10P4Cu0.3 spherical amorphous powders with good amorphous forming ability were prepared by regulating the material composition and the particle size distribution using gas atomization.
Fe77.7Si8B10P4Cu0.3 amorphous powder compacts with high relative density (rho r = 94%), high saturated magnetic induction (Bs = 1.34 T), and high permeability (mu = 163 at 20 kHz) were fabricated by spark plasma sintering. In this work, Fe77.7Si8B10P4Cu0.3 spherical amorphous powders with good amorphous forming ability were pre-pared by regulating the material composition and the particle size distribution by gas atomization at first. The effect of sintering temperature (Ts) on the structure and magnetic properties of powder compacts was system-atically investigated. The powder compacts sintered at Ts of 696-712 K were found to remain amorphous structure and exhibit optimal structural and magnetic performance, due to the high temperature and high pressure employed in SPS with high heating rate. These results are promising for the applications of Fe-based amorphous powder alloys in soft magnetic devices requiring tens of kilo-hertz frequency.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available