Journal
METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE
Volume 47, Issue 2, Pages 1217-1227Publisher
SPRINGER
DOI: 10.1007/s11663-016-0599-8
Keywords
-
Ask authors/readers for more resources
The laboratory experiments of alumina inclusions modified by calcium treatment in Al-killed steel were carried out at 1873 K (1600 degrees C), and the inclusions in steel samples were characterized at 1, 5, and 10 minutes after calcium addition. The results show that the type of inclusions after calcium treatment was determined by the sulfur and T.O contents of steel. CaS-Al2O3 inclusions were obtained in steels with high sulfur and low T.O contents. The mass ratio between CaS and Al2O3 was determined by T.Ca and T.O contents of steel. The influence of holding time after calcium addition on the composition of inclusions was negligible. The thermodynamics for the formation of CaS-Al2O3 inclusions after calcium treatment was discussed, and a simple formation mechanism was proposed. Moreover, the CaO, Al2O3, and CaS contents in the inclusions were predicted through the sulfur, total calcium (T.Ca), and T.O contents, and it was found that the CaO content decreases with increasing S/T.O, while (pctCaS)/(pctAl(2)O(3))(1/3) increases with increasing T.Ca/T.O. (C) The Minerals, Metals & Materials Society and ASM International 2016
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available