4.4 Article

Effects of Surface Oxidation on the Magnetic Properties of Fe-Based Amorphous Metal Powder Made by Atomization Methods

Journal

ELECTRONIC MATERIALS LETTERS
Volume -, Issue -, Pages -

Publisher

KOREAN INST METALS MATERIALS
DOI: 10.1007/s13391-023-00455-y

Keywords

Amorphous metal powder; Soft magnetic; Surface oxidation; High permeability

Ask authors/readers for more resources

Fe-based amorphous metal powders were prepared using different atomization methods, and their magnetic properties were characterized. The amorphous metal powder manufactured using the high-speed water screen atomization process had lower eddy current loss and higher initial permeability due to the formation of a thin and uniform oxide layer. The magnetic cores fabricated with the amorphous powders produced by the high-speed water screen atomization method exhibited smaller coercive field and lower core loss values.
The demand for soft magnetic amorphous metal powders with high saturation magnetization values and low energy loss has increased to achieve high-performance inductors for mobile electronic devices. In this study, Fe-based Fe92.3Si3.5B3.0C0.7P0.5 (wt.%) amorphous metal powders were prepared using different atomization methods for controlling the surface oxidation of the metal alloy powder. Conventional high-pressure water atomization and the newly developed high-speed water screen atomization methods were used for preparation. Regardless of the preparation methods, both alloy powders were amorphous, and their magnetic flux density (Bs) values were more than 165 emu/g. Compared to the powders from the conventional high-pressure water atomization method, the amorphous metal powder manufactured using the high-speed water screen atomization process had lower eddy current loss because of the formation of a thin and uniform oxide layer. Furthermore, the magnetic properties of the consolidated magnetic cores fabricated with the amorphous powders produced by the highspeed water screen atomization method using compact-pressing techniques were characterized. Magnetic powders with fewer surface oxidation layers exhibited increased initial permeability and a smaller coercive field, leading to a lower core loss value. The magnetic core made from Fe92.3Si3.5B3.0C0.7P0.5 (wt.%) amorphous powder with an oxide content of 0.12 (wt.%) using the high-speed water screen atomization method exhibited an initial permeability of 25 in the frequency range up to 5 MHz, and a loss of 237 mW/cm(3) with B-m = 0.2 T at 1 MHz. [GRAPHICS] .

Authors

I am an author on this paper
Click your name to claim this paper and add it to your profile.

Reviews

Primary Rating

4.4
Not enough ratings

Secondary Ratings

Novelty
-
Significance
-
Scientific rigor
-
Rate this paper

Recommended

No Data Available
No Data Available