Comparison of Tribological Characteristics of AA2024 Coated by Plasma Electrolytic Oxidation (PEO) Sealed by Different sol-gel Layers

The application of sol-gel on plasma electrolytic oxidation (PEO) coatings can increase wear resistance by sealing the surface defects such as pores and cracks in the outer layer of the PEO layer and strengthen the coating. Four different sol-gel formulations based on precursors-(3-glycidyloxypropyl)trimethoxysilane (GPTMS), methyltriethoxysilane (MTES), methacryloxypropyltrimethoxysilane (MAPTMS), (3-aminopropyl)triethoxysilane (APTES), and zirconium(IV) propoxide (ZTP) along with tetraethoxysilane (TEOS)-were used to seal PEO pores, and the samples were tested tribologically. A sliding reciprocating tribometer was used to carry out a wear test with an alumina ball as the counter body in two different conditions: (a) 2.5 N load for 20 min, and (b) 3 N load for 40 min. The coefficient of friction and wear rate as volume loss per unit sliding length were obtained for all sol-gel-sealed specimens and unsealed PEO-coated and bare AA2024 substrate. 3D mechanical profilometer surface scans were used to compare the depth of wear traces. The elemental color mapping using SEM and EDS revealed that silicon remains present in the wear tracks of PEO coatings sealed with sol-gel layers containing GPTMS (PSG) and ZTP (PSG-ZT). GPTMS (PSG) was able to fill the pores of the PEO layer efficiently due to its cross-linked network. Moreover, sol-gel containing ZTP (PSG-ZT) was deposited as a thick layer on top of the PEO layer which provided good lubrication and resistance to wear. However, other sol-gel formulations (PSG-MT and PSG-AP) were worn out during tests at a higher load (3 N). The most stable friction coefficient (COF) and specific wear rates were observed with sol-gels with GPTMS and ZTP.

Automated summary

The application of sol-gel on PEO coatings can enhance wear resistance by sealing surface defects. Different sol-gel formulations were used to seal PEO pores, and the sol-gel with GPTMS and ZTP showed good lubrication and wear resistance.