Ethanol Dehydration to Ethylene over High-Energy Facets Exposed Gamma Alumina

Highly efficient and stable catalysts are among the key factors in industrial ethanol dehydration to ethylene. Among the widely studied catalysts, alumina is the most suitable for industrial application. In this study, novel gamma alumina was synthesized by solvent protection and a hydrothermal procedure. HRTEM, XRD, FT-IR, NH3-TPD, H-D exchange, and Si-29 MAS NMR were employed to compare the difference in physicochemical properties between the novel gamma alumina and commercial alumina. Characterization results show that the as-synthesized novel gamma alumina mainly exposes the high-energy crystal plane (111) while the commercial alumina mainly exposes the thermostatically stable (110) crystal plane. The dominating (111) plane, according to the characterizations, endows the novel gamma alumina with a higher density of surface hydroxyl groups, higher acid content, and higher surface energy compared to the commercial alumina. The catalytic performance of the two catalysts for industrial ethanol dehydration to ethylene was studied. The novel (111) plane-exposed alumina showed a higher yield of ethylene than commercial alumina under the same reaction conditions. This could be related to the difference in atomic arrangement and the unsaturated aluminum coordination of different crystal planes. Stability testing under severe reaction conditions (450 & DEG;C, 1 MPa, 4 h(-1)) indicates that novel gamma alumina shows better stability (catalyst life cycle increased by 50%) and produces less acetaldehyde as a byproduct. The effects of steam treatment on the catalytic performance were further investigated. The surface acidity and the catalytic performance of novel gamma alumina present a volcanic curve with the increase in steam treatment temperature. Under the optimal water vapor treatment temperature of 650 & DEG;C, the conversion of ethanol and selectivity of ethylene were both higher than 99%.

Automated summary

Novel gamma alumina was synthesized by solvent protection and a hydrothermal procedure. The as-synthesized gamma alumina mainly exposes the high-energy crystal plane (111) and shows higher density of surface hydroxyl groups, acid content, and surface energy compared to commercial alumina. The novel gamma alumina exhibited higher yield of ethylene and better stability in industrial ethanol dehydration to ethylene, and steam treatment significantly affected its surface acidity and catalytic performance.