CERAMICS INTERNATIONAL
Volume 41, Issue 2, Pages 2582-2589Publisher
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2014.11.006
Keywords
Carbon/carbon composites; Coating; Supersonic atmosphere plasma spraying; Pre-oxidation; Ablation
Categories
Funding
- National Natural Science Foundation of China [51272213, 51221001, 51202093]
- Research Fund of the State Key Laboratory of Solidification Processing (NWPU), China [98-QZ-2014]
Ask authors/readers for more resources
To improve ablation resistance of carbon/carbon (C/C) composites at high temperature, ZrB2-SiC coating was prepared on surface of SiC-coated C/C composites by supersonic atmosphere plasma spray. The coated C/C composites were pre-oxidized in air at 1373 K. In the present work, the influence of pre-oxidation treatment on the microstructure and ablation resistance of ZrB2-SiC coating was investigated. Ablation resistance of coated C/C composites was tested in oxyacetylene torch environment with the heat flux of 2400 kW/m(2). Results show that the liquid glass phase seals defects in the as-sprayed coating after pre-oxidation for 15 min and a dense coating is obtained. The pre-oxidation coating can protect C/C composites for 90 s, which is due to the formation of a dense oxides layer and the molten ZrO2 layer. (C) 2014 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available