Fouling characteristics of microcrystalline cellulose during cross-flow microfiltration: Insights from fluid dynamic gauging and molecular dynamics simulations

The fouling behaviour of microcrystalline cellulose (MCC) particles on polyethersulfone (PES) membranes was investigated using fluid dynamic gauging (FDG) and molecular dynamics (MD) simulations. Experimental cross-flow microfiltration (MF) of a dilute MCC suspension at 400 mbar transmembrane pressure using 0.45 mu m PES membranes revealed an estimated fouling layer thickness of 616 +/- 5 mu m for both fouled and re -fouled membranes at an applied shear stress of 37 +/- 2 Pa. A decline in pure water flux was observed after each membrane cleaning and flushing procedure, indicating that highly resilient layers were formed close to the membrane surface. A possible explanation for the formation of resilient cellulose layers was obtained through MD simulations of the free energy profiles, which predicted deep energy minima at close interparticle separations of the cellulose-cellulose and cellulose-PES systems. The consequence of this energy minima is that attractive and repulsive forces are in balance at a specific distance between the particles, suggesting high binding energy at close interparticle distances. This implies that a certain force is needed to remove the layer or redisperse the cellulose particles. MD simulations also suggested that contributions made by repulsive hydration forces negatively influenced the adsorption of cellulose particles onto the PES membrane. These results highlight how experimental FDG measurements, when complemented with MD simulations, can provide insights into the fouling behaviour of an organic model material during cross-flow filtration.

Automated summary

The fouling behavior of microcrystalline cellulose (MCC) particles on polyethersulfone (PES) membranes was investigated through fluid dynamic gauging (FDG) and molecular dynamics (MD) simulations. Experimental cross-flow microfiltration of a dilute MCC suspension using 0.45μm PES membranes revealed the formation of a resilient fouling layer with a thickness of 616 +/- 5 μm. MD simulations indicated that deep energy minima between cellulose and PES caused high binding energy and the presence of repulsive hydration forces hindered the adsorption of cellulose particles onto the PES membrane.