Correlation between micro-to-macro mechanical properties and processing parameters on additive manufactured 18Ni-300 maraging steels

Journal

JOURNAL OF ALLOYS AND COMPOUNDS
Volume 960, Issue -, Pages -

Publisher

ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2023.171031

Keywords

Maraing steel; Additive manufacturing; Processing parameter; Maraging steel; Microstructure; Mechanical properties

Ask authors/readers for more resources

The 18-Ni 300 maraging steels with bulk cuboidal shape were fabricated by selective laser melting (SLM) to investigate the relationship between micro-to-macro mechanical properties and processing parameters. The results showed that the relative density of the as-built specimens was influenced by the laser power, scanning rate, and volume metric energy density (VED). The micro Vickers hardness and yield strength of the specimens were also affected by the relative density and VED.
The 18-Ni 300 maraging steels with bulk cuboidal shape were fabricated by selective laser melting (SLM) to understand correlation between micro-to-macro mechanical properties and processing parameters. The as-built specimens fabricated under various laser power and scanning rate conditions were composed of & alpha; martensite phase with cellular arm spacing of 0.2 - 0.5 & mu;m. The relative density of as-built specimens increased from 89.14% to 99.86%, depending on volume metric energy density (VED), laser power, and scanning rate, but it is more affected by the VED and laser power than the scanning rate. For porous spe-cimens fabricated under lower VED than 73 J/mm3, the laser power had a greater impact on relative density than VED, whereas relative density of specimens had a positive correlation with VED in the range of 75 - 93 J/mm3 and reached full density. Micro Vickers hardness tended to decrease with increasing VED and relative density in porous specimens, whereas in the full dense specimens, micro Vickers hardness gra-dually increased with increasing VED. The contrast in micro hardness between porous and dense specimens was attributed to nanoprecipitation affected by intrinsic heat treatment during SLM. Compression test demonstrated that yield strength strongly correlated with relative density, gradually increasing to 1.13 GPa as the specimens reached full density. From the investigation, this study provided an optimized SLM pro-cessing condition for high strength as-built 18Ni-300 maraging steel.& COPY; 2023 Elsevier B.V. All rights reserved.

Authors

I am an author on this paper
Click your name to claim this paper and add it to your profile.

Reviews

Primary Rating

4.7
Not enough ratings

Secondary Ratings

Novelty
-
Significance
-
Scientific rigor
-
Rate this paper

Recommended

No Data Available
No Data Available