High strain rate superplasticity and secondary strain hardening of Al-Mg-Sc-Zr alloy produced by friction stir processing

There have been many studies on superplasticity of Al-Mg-Sc-Zr alloy with middle magnesium content in friction stir processing (FSP), while few studies on superplasticity of FSPed Al-Mg-Sc-Zr alloy with low-magnesium were researched. In this work, the microstructure of Al-3Mg-0.1Sc-0.1Zr alloy with the grain size of-1.6 mu m and high -angle grain boundaries dominated was obtained by FSP. The high-temperature tensile test was carried out, which showed that Al-3Mg-0.1Sc-0.1Zr alloy had good superplasticity in the range of 400 degrees C -500 degrees C and 3 x 10-3 s-1 -3 x 10-1 s-1, and the optimal elongation reached 1850% at 475 degrees C and 10-2 s- 1, showing a high strain rate superplasticity. The FSPed alloy had a significant secondary strain hardening ability with increasing flow stress in the failure fracture stage at higher temperature or relatively low strain rate, showing H type (continuous hardening) and C type + secondary hardening type (initial hardening then softening + secondary hardening) curves, which was mainly attributed to the concurrent grain growth at higher strain during high-temperature tension. By studying the microstructure evolution and constitutive equation, it was found that the main mech-anism of superplastic deformation was grain boundary sliding accommodated by grain boundary diffusion, the coordination mechanism was lattice diffusion. Al3(Sc, Zr) particles hindered the coarsening of grains obviously with good thermal stability, which were conducive to the realization of excellent superplastic properties.

Automated summary

In this study, the superplasticity of Al-3Mg-0.1Sc-0.1Zr alloy obtained by FSP was investigated. The alloy exhibited good superplasticity in the temperature range of 400°C-500°C and strain rate range of 3 x 10-3 s-1 - 3 x 10-1 s-1. The FSPed alloy showed significant secondary strain hardening ability and the Al3(Sc, Zr) particles hindered grain coarsening, contributing to the excellent superplastic properties.