friction welding; copper; stainless steel; response surface methodology
Ask authors/readers for more resources
This study optimized the process conditions of friction welding to obtain the highest tensile strength of the joint at 489 MPa. The formation of intermetallic compounds at the interface was identified.
By using fusion welding to weld AISI 304 austenitic stainless steel (ASS) and commercial copper, the creation of brittle intermetallic in the weld region that compromises the strength of the joints is the primary challenge. However, friction welding is a suitable method for joining these two materials because no obvious defects are produced at the joints. The joint strength is significantly influenced by the friction-welding-process variables including the pressure of friction, pressure of forging, time of friction, and time of forging. Throughout this study, a central composite factorial design-based empirical relationship-building effort was carried out to determine the tensile strengths of friction-welded AISI 304 austenitic stainless steels (ASS) and commercial copper alloys dissimilar joints from the process variables. The process conditions were optimized employing response surface methods in order to attain the joint's optimum tensile strength. This research revealed that the greatest tensile strength of the joint created with the friction pressure of 60 MPa, forging pressure of 60 MPa, friction duration of 4 s, and forging time of 4 s, correspondingly, was 489 MPa. As a result, the intermetallic formation at the interface could be identified.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available