Giant Increase of Hardness in Silicon Carbide by Metastable Single Layer Diamond-Like Coating

Silicon carbide (SiC) is one of the hardest known materials. Its exceptional mechanical properties combined with its high thermal conductivity make it a very attractive material for a variety of technological applications. Recently, it is discovered that two-layer epitaxial graphene films on SiC can undergo a pressure activated phase transition into a sp(3) diamene structure at room temperature. Here, it is shown that epitaxial graphene films grown on SiC can increase the hardness of SiC up to 100% at low loads (up to 900 mu N), and up to 30% at high loads (10 mN). By using a Berkovich diamond indenter and nanoindentation experiments, it is demonstrated that the 30% increase in hardness is present even for indentations depths of 175 nm, almost three hundred times larger than the graphene film thickness. The experiments also show that the yield point of SiC increases up to 77% when the SiC surface is coated with epitaxial graphene. These improved mechanical properties are explained with the formation of diamene under the indenter's pressure.

Automated summary

It is discovered that two-layer epitaxial graphene films on SiC can undergo a pressure activated phase transition into a sp(3) diamene structure at room temperature, which can significantly increase the hardness of SiC. The hardness increase can reach up to 100% at low loads and up to 30% at high loads. These improved mechanical properties can be explained by the formation of diamene under the indenter's pressure.