Three-Dimensional Printed Polyamide 12 (PA12) and Polylactic Acid (PLA) Alumina (Al2O3) Nanocomposites with Significantly Enhanced Tensile, Flexural, and Impact Properties

The effect of aluminum oxide (Al2O3) nanoparticles (NPs) as a reinforcing agent of Polyamide 12 (PA12) and Polylactic acid (PLA) in fused filament fabrication (FFF) three-dimensional printing (3DP) is reported herein for the first time. Alumina NPs are incorporated via a melt-mixing compounding process, at four different filler loadings. Neat as well as nanocomposite 3DP filaments are prepared as feedstock for the 3DP manufacturing of specimens which are thoroughly investigated for their mechanical properties. Thermogravimetric analyses (TGA) and Raman spectroscopy (RS) proved the nature of the materials. Their morphological characteristics were thoroughly investigated with scanning electron and atomic force microscopy. Al2O3 NPs exhibited a positive reinforcement mechanism at all filler loadings, while the mechanical percolation threshold with the maximum increase of performance was found between 1.0-2.0 wt.% filler loading (1.0 wt.% for PA12, 41.1%, and 56.4% increase in strength and modulus, respectively; 2.0 wt.% for PLA, 40.2%, and 27.1% increase in strength and modulus, respectively). The combination of 3DP and polymer engineering using nanocomposite PA12 and PLA filaments with low-cost filler additives, e.g., Al2O3 NPs, could open new avenues towards a series of potential applications using thermoplastic engineering polymers in FFF 3DP manufacturing.

Automated summary

This study reports the effects of adding aluminum oxide nanoparticles as reinforcing agents in Polyamide 12 and Polylactic acid in fused filament fabrication. The nanoparticles demonstrated positive reinforcement mechanism and achieved maximum performance improvement at specific filler loadings.